関西ペイント
バイオックスプライマーS2
Product names, manufacturer names and thinner product names are kept in Japanese so you can match them with the can label at the store or on site.
Basic Information
| Manufacturer | 関西ペイント |
|---|---|
| Use / Type | Resin: Epoxy Original (JA): 無毒防汚用特殊硬化エポキシ樹脂塗料(2液形) |
| Water-based / Solvent-based | Solvent-based, 2-component |
| 1K / 2K | 2-component (2K) |
Application Specifications
| Dilution | airless: 0–10% Brush / Roller: 0–5% |
|---|---|
| Thinner / Diluent | テクトEP内面用シンナー (thinner for tank-interior use) |
| Number of Coats | 1 coat(s) |
| Coverage (consumption) | airless: 465 g/m² Brush / Roller: 180 g/m² |
| Recoat Time (drying interval) | 5°C: Min 24 hours / Max 7 days Usable time 12 hours 10°C: Min 24 hours / Max 7 days Usable time 12 hours 20°C: Min 16 hours / Max 7 days Usable time 8 hours 30°C: Min 10 hours / Max 7 days Usable time 5 hours 40°C: Min 10 hours / Max 7 days Usable time 2 hours |
| Mixing Ratio | Base 7:Hardener (Comp. B) 1 |
| Pot Life | 12 hours (5°C) , 12 hours (10°C) , 8 hours (20°C) , 5 hours (30°C) , 2 hours (40°C) |
| Induction time (after mixing) | 10–15 minutes when applied at 5–10℃ (not needed at 10℃ or above) |
| Field Notes (JA) | ・ 標準乾燥膜厚は50µm(下塗) ・ 5〜10℃では熟成時間10〜15分が必要(10℃以上は不要) ・ 気温5℃以下・湿度85%以上では施工不可。 |
* For heavy-duty anticorrosion work, the number of coats and the film thickness are fixed by the painting specification of each project. The figures shown here are the maker's standard values.
⚠️ Please verify before use
The values above are reference values based on the manufacturer's official catalogs and technical data sheets (TDS). Specifications may change. Always check the product label and the latest official TDS before actual application.
The values above are reference values based on the manufacturer's official catalogs and technical data sheets (TDS). Specifications may change. Always check the product label and the latest official TDS before actual application.
Data source: official catalogs / technical data sheets (TDS) of 関西ペイント
Page updated: 2026-09-03