関西ペイント
耐酸テルモ
Product names, manufacturer names and thinner product names are kept in Japanese so you can match them with the can label at the store or on site.
Basic Information
| Manufacturer | 関西ペイント |
|---|---|
| Use / Type | Resin: Silicone ｜ Features: Heat-resistant Original (JA): 耐熱、耐薬品用特殊シリコン樹脂塗料(二液形) |
| Water-based / Solvent-based | Solvent-based, 2-component |
| 1K / 2K | 2-component (2K) |
Application Specifications
| Dilution | 0–5% |
|---|---|
| Thinner / Diluent | エナメルシンナー200 |
| Number of Coats | Multiple coats |
| Coverage (consumption) | airless: 140 g/m² Brush / Roller: 110 g/m² |
| Recoat Time (drying interval) | 5°C: Min 48 hours / Max 10 days Usable time 3 hours 10°C: Min 24 hours / Max 10 days Usable time 3 hours 20°C: Min 16 hours / Max 7 days Usable time 2 hours 30°C: Min 12 hours / Max 7 days Usable time 2 hours 40°C: Min 12 hours / Max 7 days Usable time 2 hours |
| Mixing Ratio | Base 8:Hardener (Comp. B) 2 |
| Pot Life | 3 hours (5°C) , 3 hours (10°C) , 2 hours (20°C) , 2 hours (30°C) , 2 hours (40°C) |
| Field Notes (JA) | ・ 常時200℃(瞬間250℃)耐熱・耐酸で煙道内面用に適する。 ・ 本来焼付形(セッティング15〜30分/20℃、焼付150〜200℃×30分) ・ 鉄面の素地調整は1種ケレンが必要。 ・ 標準膜厚75μm。 ・ 上塗すると下塗がにじむ場合は上塗を2回塗りかスプレー塗装。 |
⚠️ Cautions & Notes (Japanese original)
To avoid mistranslation of safety-critical information, the notes below are kept in the original Japanese. Please check them with a translation app, or ask a Japanese-speaking colleague. Always follow the official manufacturer TDS.
⚠️ Please verify before use
The values above are reference values based on the manufacturer's official catalogs and technical data sheets (TDS). Specifications may change. Always check the product label and the latest official TDS before actual application.
The values above are reference values based on the manufacturer's official catalogs and technical data sheets (TDS). Specifications may change. Always check the product label and the latest official TDS before actual application.
Data source: official catalogs / technical data sheets (TDS) of 関西ペイント
Page updated: 2026-08-25