エスケー化研
水性ハイブリッドシーラー
Product names, manufacturer names and thinner product names are kept in Japanese so you can match them with the can label at the store or on site.
Basic Information
| Manufacturer | エスケー化研 |
|---|---|
| Use / Type | Use: Primer / Undercoat ｜ Resin: Epoxy Original (JA): 広範囲適用型水性特殊エポキシ樹脂シーラー |
| Water-based / Solvent-based | Water-based, 2-component |
| 1K / 2K | 2-component (2K) |
Application Specifications
| Dilution | Ready-mixed |
|---|---|
| Thinner / Diluent | Ready-mixed (No thinning required) |
| Number of Coats | 1–2 coat(s) |
| Coverage (consumption) | 0.08–0.20 kg/m² (1–2 coats' worth) (素地別: 窯業系サイディングボード0.08–0.12 · 1 coat(s)/extruded cement board 0.08–0.12 · 1 coat(s)/concrete · cement mortar 0.10–0.20 · 1–2 coat(s)/calcium silicate board 0.15–0.20 · 1–2 coat(s)) |
| Recoat Time (drying interval) | 23°C: within the step 3 or more, between steps 6 or more 7 days or less (hours) |
| Mixing Ratio | Base (Comp. A) 14:Hardener (Comp. B) 1 (14:1) |
| Pot Life | 4 hours (23°C) |
| Field Notes (JA) | ・ 2液形。混合後は可使時間(23℃で4時間)以内に使い切る。 ・ 調合は主剤100:硬化剤7.14(重量比)を厳守。小分け時は計量器で計量する。 ・ 【訂正記録】2026-08-04まで素地別所要量の押出成形セメント板を0.08〜0.20と収録していたが、公式カタログの「素地別所要量の目安」は0.08〜0.12。ポットライフも未収録だった。 |
⚠️ Cautions & Notes (Japanese original)
To avoid mistranslation of safety-critical information, the notes below are kept in the original Japanese. Please check them with a translation app, or ask a Japanese-speaking colleague. Always follow the official manufacturer TDS.
⚠️ Please verify before use
The values above are reference values based on the manufacturer's official catalogs and technical data sheets (TDS). Specifications may change. Always check the product label and the latest official TDS before actual application.
The values above are reference values based on the manufacturer's official catalogs and technical data sheets (TDS). Specifications may change. Always check the product label and the latest official TDS before actual application.
Data source: official catalogs / technical data sheets (TDS) of エスケー化研
Page updated: 2026-08-25